LNP™VERTON™ NV0081EV_GY7E149 Compound datasheet
 

LNP™VERTON™ Compound NV0081EV_GY7E149

Americas: OBSOLETE

 
Preliminary data for 40% long fiber single pellet non-halogen FR color filled PC/ABS
 

Property
 
TYPICAL PROPERTIES (1)
MECHANICAL
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min
930
kgf/cm²
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min
930
kgf/cm²
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min
0.9
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
0.9
%
ASTM D 638
Tensile Modulus, 50 mm/min
125000
kgf/cm²
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
1590
kgf/cm²
ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span
1590
kgf/cm²
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
131500
kgf/cm²
ASTM D 790
Tensile Stress, yield, 5 mm/min
100
MPa
ISO 527
Tensile Stress, break, 5 mm/min
100
MPa
ISO 527
Tensile Strain, yield, 5 mm/min
0.9
%
ISO 527
Tensile Strain, break, 5 mm/min
0.9
%
ISO 527
Tensile Modulus, 1 mm/min
10750
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
152
MPa
ISO 178
Flexural Stress, break, 2 mm/min
152
MPa
ISO 178
Flexural Strain, break, 2 mm/min
1.2
%
ISO 178
Flexural Modulus, 2 mm/min
12350
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C
44
cm-kgf/cm
ASTM D 4812
Izod Impact, unnotched, -40°C
48
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
24
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -40°C
30
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
117
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
32
kJ/m²
ISO 180/1U
Izod Impact, unnotched 80*10*4 -40°C
27
kJ/m²
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
26
kJ/m²
ISO 180/1A
Izod Impact, notched 80*10*4 -40°C
29
kJ/m²
ISO 180/1A
THERMAL
Value Unit Standard
HDT, 1.82 MPa, 3.2mm, unannealed
88
°C
ASTM D 648
CTE, -40°C to 40°C, flow
2.18E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
3.79E-05
1/°C
ASTM E 831
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
89
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Density
1.536
g/cm³
ASTM D 792
Water Absorption, 24 hours
0.057
%
ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)
0.06 - 0.26
%
ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)
0.31 - 0.51
%
ASTM D 955
Density
1.53
g/cm³
ISO 1183
Water Absorption, 23°C/24hrs
0.07
%
ISO 62-1
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3)
1.5 - 1.6
mm
UL 94
Source GMD, last updated:2013/03/13
Processing

Parameter
Injection Molding
Value Unit
Drying Temperature
30 - 40
°C
Drying Time
2 - 4
hrs
Drying Time (Cumulative)
0
hrs
Melt Temperature
220 - 255
°C
Front - Zone 3 Temperature
215 - 245
°C
Middle - Zone 2 Temperature
210 - 245
°C
Rear - Zone 1 Temperature
205 - 235
°C
Mold Temperature
35 - 65
°C
Back Pressure
0.2 - 0.3
MPa
Screw Speed
12 - 40
rpm
Source GMD, last updated:2013/03/13
 
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(6) Needs hard coat to consistently pass 60 sec Vertical Burn.


Disclaimer : THE MATERIALS, PRODUCTS AND SERVICES OF SAUDI BASIC INDUSTRIES CORPORATION (SABIC) OR ITS SUBSIDIARIES OR AFFILIATES (“SELLER”) ARE SOLD SUBJECT TO SELLER’S STANDARD CONDITIONS OF SALE, WHICH ARE AVAILABLE UPON REQUEST. INFORMATION AND RECOMMENDATIONS CONTAINED IN THIS DOCUMENT ARE GIVEN IN GOOD FAITH. HOWEVER, SELLER MAKES NO EXPRESS OR IMPLIED REPRESENTATION, WARRANTY OR GUARANTEE (i) THAT ANY RESULTS DESCRIBED IN THIS DOCUMENT WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN OR APPLICATION INCORPORATING SELLER’S MATERIALS, PRODUCTS, SERVICES OR RECOMMENDATIONS.  UNLESS OTHERWISE PROVIDED IN SELLER’S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS, PRODUCTS, SERVICES OR RECOMMENDATIONS DESCRIBED IN THIS DOCUMENT. Each user is responsible for making its own determination as to the suitability of Seller’s materials, products, services or recommendations for the user’s particular use through appropriate end-use and other testing and analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller’s Standard Conditions of Sale or this Disclaimer, unless it is specifically agreed to in a writing signed by Seller.  Statements by Seller concerning a possible use of any material, product, service or design do not, are not intended to, and should not be construed to grant any license under any patent or other intellectual property right of Seller or as a recommendation for the use of any material, product, service or design in a manner that infringes any patent or other intellectual property right.

SABIC and brands marked with ™ are trademarks of SABIC or its subsidiaries or affiliates.

© 2014 Saudi Basic Industries Corporation (SABIC). All Rights Reserved.